Anti- Oxidation Graphite Crucibles for Vaporized Aluminum Vacuum Coating

Port	tianjin port
Packaging	Plywood Cases
Lead Time	20

Contact Now

Quick Details (View All)

Density	No less Than 1.88g/cm3	Compressive Strength	More Than 70MPa
Porosity	Less Than 26%	Elasticity Modulus	6-18 Gpa
Thermal Expansion Coefficient	1.47-4.25	Ash Content	Less Than 0.05%
Temperature Resistance	Less Than 4350 Degree

Product Details

anti- oxidation Graphite Crucibles for Vaporized Aluminum Vacuum Coating
www.ltgraphite.com

A: Company profile

L.T Graphite has a comprehensive product and technology portfolio that focuses on four fields of graphite - ultrafine particle graphite mould, graphite electrode, graphite crucible, as well as other products mainly made of graphite.
Graphite materials exhibit unique properties such as good electrical and thermal conductivity, heat and corrosion resistance, low friction, and reduced weight while at the same time maintaining high strength. Due to the shortage of energy and raw materials, our high performance products made from graphite are in increasingly high demand in industries. They also play a progressively important role in everyday life, thereby substituting traditional materials.

B: Our Products:

L.T Graphite crucible is divided into four categories: high purity fine particle graphite crucible, medium particle graphite crucible, silicon carbide graphite crucible and other coated graphite crucible( graphite crucible for vacuum coating of gasification aluminum )

Graphite crucible has good thermal conductivity and high temperature resistance, the use of high temperature, the thermal expansion coefficient is small, the rapid heat, quenching has a certain anti-strain properties. Right acid, alkaline solution, strong corrosion resistance, with excellent chemical stability.

Due to its excellent performance, graphite crucible is widely used in metallurgy, casting, machinery, chemical and other industrial sectors for the smelting of alloy tool steel and the smelting of non-ferrous metals and their alloys, and has good technical and economic effects.

C: Advantages:

1. High strength .As the temperature rises, the graphite strength increases
2. High temperature resistance
3. Good heat shock resistance
4. Anti-oxidation
5. Strong corrosion resistance to acid and alkali liquid
6. Good conductivity and thermal efficiency.
7. Excellent chemical stability
8. High heat conductivity
9. Mechanical shock resistance
10. Small thermal expansion coefficient

D: Four categories graphite crucible and Tech Data:

a. High purity fine particle graphite crucible

Density g/cm³	1.75-1.9
Resistivity μΩ·m	≤12
Compressive strength Mpa	≥70
Porosity %	≤26
Elasticity Modulus Gpa	6-18
Thermal expansion coefficient 10-6/ºC	1.47-4.25
Ash content %	≤0.05
Temperature resistance ºC	≤4350ºC

b. Medium particle graphite crucible

Item	Unit	2.0mm HNLT	2.0mm HNLT
Bluk Density	g/cm3	≯12	≯9
Electric Resitivity	μΩm	≮1.58	≮1.70
Compressive Strength	Mpa	≮19	≮30
Bending Strength	Mpa	≮7.8	≮13
Ash Content	%	≯0.3	≯0.3
C.T.E	10-6/ºC	≯2.0	≯2.2

c. Silicon carbide graphite crucible:a

Bulk Density g/cm³	1.9-2.1
Porosity %	10-14
Carbon Content %	30-45
Silicon Carbide content %	≥48
Temperature resistance ºC	1665

d. Coated graphite crucible

Graphite crucible for vacuum coating of gasification aluminum for example.
Is mainly suitable for under the condition of vacuum, the metal aluminum gasification and evaporation on the surface of CPP, PET, BOPP film, And forming aluminum composite film. Graphite crucibles are a large number of consumption parts during the producing process, the quality of graphite crucibles will directly affect the product quality and production cost of aluminum plating film.
L.T graphite has developed a new kind graphite composite materials, used for vacuum coating of gasification aluminum, with outstanding features: greatly improve its oxidation resistance, high bulk density and flexural compressive strength, increased abrasion resistance and hardness, reduce porosity and permeability. The wetting and erosion ability of molten aluminum liquid and gaseous aluminum molecules is weakened to a large extent, and thus the service life of the crucible is prolonged.