Density g/cm³ | 1.75-1.9 | Resistivity μΩ·m | ≤12 |
Compressive strength Mpa | ≥70 | Porosity % | ≤26 |
Elasticity Modulus Gpa | 6-18 | Thermal expansion coefficient 10-6/ºC | 1.47-4.25 |
Ash content % | ≤0.05 | Temperature resistance ºC | ≤4350ºC |
A:
Company profile
L.T Group has a comprehensive product and technology portfolio
that
focuses on four fields of graphite - ultrafine particle graphite
mould,
graphite electrode, graphite crucible, as well as other products
mainly
made of graphite.
Graphite materials exhibit unique properties such as good
electrical and
thermal conductivity, heat and corrosion resistance, low
friction, and reduced
weight while at the same time maintaining high strength. Due to
the shortage
of energy and raw materials, our high performance products made
from graphite
are in increasingly high demand in industries. They also play a
progressively
important role in everyday life, thereby substituting traditional
materials.
B: Graphite rotor
introduction
Graphite rotor is mainly used in
liquid aluminum, aluminum alloy purification
process, to improve the
purity of aluminum or aluminum alloy. It is the most
advanced treatment method in the world that mix the purification
gas and solvent,
use the rotating jet of the graphite rotor to purify the aluminum
during the
purification process,
Under high temperature aerobic conditions, in the production
process of
on - line degassing machine for fine aluminum casting,
graphite rotor has
defects of easy oxidation & break, no friction. Our team choose
high quality
reasonable ratios of graphite materials, coated with high
temperature
antioxidants which was R&D independently while no
pollution to the
Aluminum liquid. Our unique anti-oxidant graphite rotor performs
outstanding
oxidation resistance, corrosion resistance, high hardness, high compressive
strength makes continuous use for 90-120 days available, thus
effectively
reduce producing cost for customers.
C: Working
principle:
A twirling graphite rotor shatters nitrogen (or argon),
which is blown into
melting aluminum, into profuse bubbles that disperse in the
liquid metal.
Regarding gas pressure difference and surface adsorption
principle, bubbles
in the melt absorb hydrogen
and oxidation slag inclusion which are taken out
to surface of the melt with the rise of the bubbles, so that the
melt can be purified.
D: Working
conditions:
Put the impeller end and part of the shaft of a
graphite rotor into
690°C-780°C Aluminum liquid, rotation speed 500 RPM, 1-2 hours at
a time,
work for 4-6 times per day. graphite rotor can also work
continuously according
to the working condition of the equipment.
E:Product
features:
1. Our graphite rotor is made of
high-quality graphite material.
2. After special anti-oxidant
treatment, the service life could reach 5 -10 times
compared to ordinary market graphite rotor.
3. Our graphite rotor widely used
in high purity aluminum industry and
aluminum alloy casting industry.
Supporting equipment | Service life | Output product |
French online degassing equipment | 90 days more | High purity aluminum |
US Online degassing equipment | 90 days more | High purity aluminum |
Domestic online degassing equipment | 60~90 days | High purity aluminum;aluminum alloy |
Flow groove online degassing equipment | 30~45 days | aluminum alloy |
Moveable online degassing equipment | 30~45 days | aluminum alloy |
High purity aluminium by segregation equipment |
24 work
time:60~80 furnace; 12 work time80~100 furnace |
High purity aluminum |
Huixian Industrial Cluster District, Baiquan Town, Huixian, Henan, China