MOQ | 55 Kilogram/Kilograms |
Port | shanghai |
Packaging | woven bag |
Lead Time | - |
Place of Origin | Zhejiang, China (Mainland) | Application | Refractory |
Width | 610/1220mm | Length | Customized |
Grade | COM (Common) | Chemical Composition | AL2O3 |
Ultimate Strength (u2265 MPa) | u2265200000 | Working Temperature | 1260-1350 |
Fiber Diameter | 3-5um | Thermal Conductivity | 0.075~0.085 |
Density (kg/mu00b3 ) | 128 | Shrinkage (1800u2109, 3h) | 3%~3.5% |
Brand Name | gt | Model Number | GT8.3 |
Maximun Service Temp(u2103) | 0.45u00b10.05/Ceramic Fiber Paper | Product name | thermal fiber Heat Insulating Aluminum silicate ceramic fiber paper |
Water Content% | u22641/Ceramic Fiber Paper | Nominal Volume Density(kg/m3)u00b115 | 200-300/Ceramic Fiber Paper |
Tensile Strength (Pa) | u2265200000/Ceramic Fiber Paper | AL2O3% | 45-55/Ceramic Fiber Paper |
SiO2% | 51-52/Ceramic Fiber Paper | Fe2O3% | <1.2 - <0.2/Ceramic Fiber Paper |
K2O+Na2O% | <0.5 - <0.2/Ceramic Fiber Paper | thickness | 0.5mm-6mm/Ceramic Fiber Paper |