Application | Heat Insulation | Thickness | 13-100mm |
Width | 600/1000mm | Length | 900/1000/1200mm |
Grade | HA (High Aluminum) | Chemical Composition | Al2O3,SiO2,etc |
Ultimate Strength (u2265 MPa) | 0.5 | Working Temperature | 1100 |
Fiber Diameter | 3-4.5um | Thermal Conductivity | 0.13-0.19(w/m.k)(800-1000Degree) |
Shrinkage (1800u2109, 3h) | -3(24hours) | Place of Origin | Shandong, China |
Model Number | LKT1260 | Brand Name | LKT |
Color | White | Density(kg/m3) | 280 |
Linear shrinkage after firing%(u2103*24H) | u22644 (1000u2103) | Ignition lost (at1000u2103*5hr)LOI% | 5 |
Rupture strength(Mpa) | 0.5 |