MOQ | 200 Kilogram/Kilograms |
Place of Origin | Zhejiang, China | Brand Name | Ruichem |
Model Number | RJ-WP03E | Appearance | Milky white liquid |
Solid Content | 40% | pH | 6-7 |
Density 25u2103 (g/cm3) | about 1 | Solvent | Water |
Dilution ratio | 1:5~1:8 | Type | Other Waterproofing Materials |
Description:
RJ-WP03E is a
non-ionic silane / siloxane emulsion. This product is a
excellent penetration waterproofing agent, when RJ-WP03E is
coated on the surface of the substrate, it will penetrate into
the substrate and does not block capillary. Hydrophobic film is
formed by the reaction of reactive groups,and combined with
hydroxyl groups in the substrate to form a Si-R siloxane chain.
It will fill the micro pores, improve the strength of the
substrate. After the construction, its water contact angle can
reach 120°or more with high water resistance ability.RJ-WP03E
is the ideal choice for building materials and stone surface
protection.
Technical Index:
Appearance |
Milky white liquid |
Active Content |
40% |
Centrifugal Stability |
No layers after centrifuge at 3000 rpm for 15 min |
pH |
6-7 |
Solvent |
Water |
Features:
*Low molecular structure, can
penetrate into the substrate surface to provide protection,
penetration depth≥2 mm.
*Greatly reduce the water
absorption of the substrate, resist corrosion and acid
rain
*Not affect the appearance of
the substrate, improve anti-efflorescence ability and prolong
the life of the substrate.
*Water-Soluble, low VOC.
Application:
*Interior and exterior surface of buildings.
*Brick, concrete and wood.
*Natural stone and artificial stone.
*Highway and airport pavement.
*Ancient artifacts and ancient buildings.
Use guide:
Diluted RJ-WP03E emulsion to 4%-8%(Active Content), added 5-10
fold water to RJ-WP03E and mixed uniformly before use. First
clean the substrate surface, methods of application include
roller, brush or a low pressure sprayer. To obtain a good
waterproof performance, bursh or spray the substrate 2
times.The neutral substrates such as stone, added 0.5% organic
tin catalyst (by active content weight) to the diluted emulsion
before use. After the construction, substrate need 7 days
protection ensure to silicone resin fully cured.