MOQ | 20 Metric |
Place of Origin | Liaoning, China | Shape | brick |
Material | Magnesia,Graphite,Binding Agent etc. | SiO2 Content (%) | As requested |
Al2O3 Content (%) | As requested | MgO Content (%) | 70-80% |
CaO Content (%) | As requested | Refractoriness (Degree) | Common (1580°< Refractoriness< 1770°) |
CrO Content (%) | As requested | SiC Content (%) | As requested |
Model Number | CX-MT | Brand Name | Chuangxing |
Product name | Refractory Magnesia Carbon Bricks | Application | Industrial Furnaces |
Color | Black | Size | 230mm*114mm*65/75mm |
MgO | 70%~80% | C | 10-18% |
Apparent Porosity | 4-6% | BULK DENSITY | 2.7~2.7g/cm3 |
Cold Crushing Strength | 25-45 Mpa | H.MOR | 6-10 Mpa |