MOQ | 1000 Kilogram/Kilograms |
Place of Origin | Shandong, China | Shape | Block |
Material | Alumina Block | SiO2 Content (%) | 38.2 |
Al2O3 Content (%) | 48-55 | MgO Content (%) | - |
CaO Content (%) | 0.4 | Refractoriness (Degree) | 1770u00b0< Refractoriness< 2000u00b0 |
CrO Content (%) | - | SiC Content (%) | - |
Model Number | SK26 SK38 TS80 SL92.... | Brand Name | LKT |
Item | high alumina fire bricks | Apparent porosity(%) | 20.0-22.0 |
Cold Crushing Strength (MPa) | 45-48 | Modulus of Rupture (kg/cm2) | 70-80 |
Na2O+K2O+Li2O (%) | 0.5 | Refractoriness | 1785-2000 |
Bulk density(g/cm3) | 2300-2350 2400-2450 2550-2650..... | Modulus of Rupture | 70-80 80-90 90-100 150-180 |
Refractory materials | High alumina friebricks Clay bricks | aluminum oxide powder | 48-55% 70-75% 85% 92% |