MOQ | 5 Ton/Tons |
Place of Origin | Hainan, China | Shape | Powder |
Material | alumina oxide | SiO2 Content (%) | 5% |
Al2O3 Content (%) | 83% | MgO Content (%) | 5% |
CaO Content (%) | 2% | Refractoriness (Degree) | 1770°< Refractoriness< 2000° |
CrO Content (%) | 0 | SiC Content (%) | 0 |
Model Number | DRFG | Brand Name | DD |
main content | alumina oxide | BD G/CM3 | 2.7 |
Compressive strength Mpa | 25 min. | Crushing strength Mpa | 5 min. |
Thermal conductivity 1000u2103 | 0.85 W/m/deg K | Water Addition | 12-14% |
refractoriness | 1930 | type | Coils Grouting |
application | induction furnace | advantage | good refractoriness |