MOQ | 1000 kg |
Packaging | 25kg/bag |
Lead Time | 14 days |
Polyamide 6 reinforced with 45% Glass Fibers that is PA GF45, medium viscosity and dimensional stability, this PA6 plastic material has excellent rigidity and high tensile and compressive strength successfully applying to engineering structure parts of mechanical engineering and in the automotive industry.
Typical Application of PA6 GF45 (A1011I)
PA6 GF45 is used in turbines, propellers, screws, nuts, washers and other components with high rigidity and dimensional stability and heat-resistant aging, as well as fishing tackle reels, racket frames and other components with high mechanical strength, good toughness, higher tensile and compressive strength.
Other Details of PA6 GF45 (A1011I)
Physical Property
Ash |
(15.0% 1 ISO3451/1) |
Conditioned |
600°C*2h |
Density |
(1250Kg/m3 1 ISO1183) |
Conditioned |
23°C |
Shrinkage Parallel Flow |
(0.5-0.7 % 1 ISO294-4) |
Shrinkage Vertical Flow |
(0.7-1.1% I ISO294-4) |
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527) Conditioned |
5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned |
1.0J |
Notched Impact Strength (125 0MPa I ISO527) Conditioned |
2mm/min |
Flexural Strength (190MPa 1ISO178) Conditioned |
2mm/min |
Flexural Modulus (5700 MPa I ISO178) Conditioned |
5mm/ min |
Thermal Property
Melting Point |
(220°C I ISO11357) |
Hot Deformation Temperature |
(175*C I ISO75) |
Conditioned |
1.8MPa |
Flammability Class |
(HB 1UL94) |
Conditioned |
mm |
Injection Molding Conditions
Drying Temperature |
130°C |
Drying Time |
3h |
Cylinder Temperature |
240-260°C |
Nozzle Temperature |
240-260*C |
Tooling Temperature |
80*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation!
As one of engineering plastic manufacturers, Anmei provides pa6 plastic material, modified polyolefin, master batches and etc. For more information, please feel free to contact us!