MOQ | 1000 kg |
Packaging | 25kg/bag |
Lead Time | 14 days |
PA 6 GF50 is a fiber reinforced plastic made of nylon 6 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added.
Typical Application of PA6 GF50 (A1011J)
PA GF50 is used to manufacture high-strength and high wear-resistant structural parts of machinery, vehicles, electronics, sports equipment and other fields. We know that pa6 50gf composite material takes both strength and toughness into consideration, which is exactly what the suspension control arm needs.
Processing Detail of PA6 GF50 (A1011J)
Other Details of pa6 6 gf50(A1011J)
Physical Property
Ash |
(15.0% 1 ISO3451/1) |
Conditioned |
600°C*2h |
Density |
(1250Kg/m3 1 ISO1183) |
Conditioned |
23°C |
Shrinkage Parallel Flow |
(0.5-0.7 % 1 ISO294-4) |
Shrinkage Vertical Flow |
(0.7-1.1% I ISO294-4) |
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527) Conditioned |
5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned |
1.0J |
Notched Impact Strength (125 0MPa I ISO527) Conditioned |
2mm/min |
Flexural Strength (190MPa 1ISO178) Conditioned |
2mm/min |
Flexural Modulus (5700 MPa I ISO178) Conditioned |
5mm/ min |
Thermal Property
Melting Point |
(220°C I ISO11357) |
Hot Deformation Temperature |
(175*C I ISO75) |
Conditioned |
1.8MPa |
Flammability Class |
(HB 1UL94) |
Conditioned |
mm |
Injection Molding Conditions
Drying Temperature |
130°C |
Drying Time |
3h |
Cylinder Temperature |
240-260°C |
Nozzle Temperature |
240-260*C |
Tooling Temperature |
80*C |
As one of masterbatch producers, Anmei provides pa6 plastic material, modified polyolefin, master batches and etc. For more information, please feel free to contact us!