MOQ | 5 Ton/Tons |
Place of Origin | Shanghai, China | Grade | Q235, S235JR/S355JR/SS400/SS490/ST-52/ST-37 |
Technique | Hot Rolled, Hot Rolled | Thickness | 5-34mm |
Application | construction, factory | Length | 12m or cut as your request |
Standard | ASTM, AISI, ASTM, BS, DIN, GB, JIS | Flange Width | 100mm-408mm |
Flange Thickness | 8-35mm | Web Width | 100mm~900mm |
Web Thickness | 6-21mm | Brand Name | Masteel ,Rizhaosteel ,Jinxisteel,Tiansteel |
Model Number | 100*100-900*300 | Product | standard sizes h beam iron factory at lows |
Carbon Content | A36/C(0.12-0.20)% S355JR/C(0.12-0.20)% | Yield Strength | A36/235-280MPa S355JR/335-360MPa |
Strength of Extension | A36/420MPa S355JR/485MPa | Manganese Content | A36/Mn(0.45)% S355JR/Mn(1.35)% |
Silicon Content | A36/235B/Si(≥0.19)% S355JR/Si(≥0.002)% | Phosphorus Content | A36/P(0.03)% S355JR/P(0.012)% |