Overview
Stainless 440C is a high-carbon martensitic stainless steel. As a martensitic stainless steel, 440C is magnetic and can be hardened by heat treatment. The high carbon content in 440C provides high hardness and strength. Despite this carbon content, the chromium content is sufficient to retain its stainless characteristics. Martensitic steels are commonly used in applications where high strength and moderate corrosion resistance is required.
Application
Valve Seats
Surgical Instruments
Bearings
Bushings
Nozzles
Structural Aircraft Parts
440 Stainless Pipe Chemical Composition
440 Stainless Steel Chemical Composition, % | |||||||||
ASTM | Steel | AISI (UNS) | C | Si (≤) | Mn (≤) | P (≤) | S (≤) | Cr | Mo (≤) |
ASTM A276/A276M | 440 Steel | 440A (S44002) | 0.60-0.75 | 1 | 1 | 0.04 | 0.03 | 16.0-18.0 | 0.75 |
440B (S44003) | 0.75-0.95 | 1 | 1 | 0.04 | 0.03 | 16.0-18.0 | 0.75 | ||
440C (S44004) | 0.95-1.20 | 1 | 1 | 0.04 | 0.03 | 16.0-18.0 | 0.75 |
Physical Properties
SS440 Physical Properties | |
Density (g/cm3) | 7.8 |
Melting point (℃) | 1370-1480 |
Specific heat capacity, J/(Kg·K) | 460 (0-100 ℃) |
Electrical resistivity (μΩ·m) | 0.6 (20 ℃) |
Elastic modulus (GPa) | 200 |
Thermal conductivity (W/m·K) | 24.2 (100 ℃) |
Coefficient of thermal expansion | 10.2 (0-100 ℃) |
Mechanical Properties Stainless Steel 440
Mechanical Properties | |||||
Grade (UNS) | Tensile Strength (MPa) ≥ | Yield Strength, 0.2%, ≥ (MPa) | Elongation in 50 mm (%) ≥ | Reduction in area (%) | Hardness |
440A (S44002) | 725 | 415 | 20 | 95 HRB | |
1790 | 1650 | 5 | 20 | 51 HRC | |
≤ 965 | |||||
440B (S44003) | 740 | 425 | 18 | 96 HRB | |
1930 | 1860 | 3 | 15 | 55 HRC | |
≤ 965 | |||||
440C (S44004) | 760 | 450 | 14 | 97 HRB | |
1970 | 1900 | 2 | 10 | 57 HRC | |
≤ 965 |