INR18650-2200mAh battery,2000mAh Li-ion battery supplier,lithium ion battery for power tool,power tool lithium ion battery supplier
2200mAh Li-ion battery Product Details:
|
Items |
Specifications |
|
1 |
Model |
INR18650-2200 |
|
2 |
Can Material |
Ni-Iron |
|
3 |
Rated Capacity |
2200 mAh(0.2C5A) |
|
4 |
Nominal Voltage |
3.7V |
|
5 |
Max. Charge Voltage |
4.2 V |
|
6 |
Discharge Cut-off Voltage |
2.75V |
|
7 |
Max. Charge Current |
1 C5A |
|
8 |
Standard Discharging Current |
0.5 C5A |
|
9 |
Max. Continuous Discharge Current |
11 A |
|
10 |
Max. Pulse Discharge Current |
30A( 2s pulse ) |
|
11 |
Max. Diameter(include PET) |
≤18.40 mm |
|
12 |
Max. Height (include PET) |
≤65.50mm |
|
13 |
Weight (Approx.) |
44.0g |
|
14 |
Impedance (Max. at 1000Hz、charged status) |
≤ 18 mΩ |
|
15 |
Charge Method (CC/CV) |
Standard |
0.2 C5A×5hrs |
Quick |
1 C5A×2.5hrs. |
||
16 |
Operating Temperature |
Charge |
0℃~45℃ 32oF~113oF |
Discharge |
-10℃~60℃ -4oF~140oF |
||
Storage |
-20℃~45℃ -4oF~113oF |
Characteristic of 2200mAh Li-ion cylindrical battery
Without special instructions, the following tests should be done under the condition of : temperature(23℃±3℃), atmospheric pressure (86KPa~106KPa), relative humidity (45%~85%), and the tests should be done within two weeks after receiving the products.
the definitions of some nomenclatures of this specification
standard Charge: Charge with current 0.2C5A to limit charge voltage under the condition of23℃±3℃ surrounding temperature, then change to charge with constant voltage till the current less than or equal to 0.02C5A.
Electrical Characteristic for Cylindrical Rechargeable Electric vehicle li-ion Battery
NO. |
Item |
Standard |
Test Method |
1 |
Discharge rate capabilities |
A)1 C5A ≥97% B)5 C5A ≥95% |
Standard charged under the condition of normal atmospheric pressure and the environmental temperature of 23℃±3℃ and45%~85%RH, then rest for 30mins and discharge at1C5A、5 C5A、10 C5A to the discharge cut-off voltage respectively. Charge/discharge cycle can be conducted for 3times before meeting the Standards(the same below) |
2 |
capacity retention and recovery |
Residualcapacity≥94 % Recoverablecapacity≥*98% |
Standard charged under the condition of normal atmospheric pressure and the environmental temperature of 23℃±3℃, Stored for 28 days, then discharge at 0.2 C5A to 2.50Vmeasuring residual capacity; Then standard charge/discharge measure recoverable capacity. |
|
Low TemperaturePerformance |
discharge capacity≥85% rated capacityno distortion and no rupture |
The cell shall be charged in accordance with the standard charge. Then stored in the temperature of -10℃±1℃ for4h, Discharge at the constant current of 0.2C5A down to the end-of-discharge voltage 2.750V. |
4 |
Cycle Life |
Charge: The cell shall be charged in accordance with RapidCharge condition. rest for 10mins.Discharge : 5C5A discharge to 2.75V, one cycle is finished, then rest for 30mins. Then repeat above steps, when capacity is less than 80% of initial capacity, the battery life is over. |
Safety Characteristic of bicycle 18650 battery
NO. |
Item |
Standard |
Test Method |
1 |
Overcharge |
No fire、No explosion |
After standard charge, rest for 10mins; then charge at constant current of 3C5A to 10V.(or charge at 3C5A for 90mins). |
2 |
Forced discharge |
No fire、No explosion |
The battery to be discharged with standard discharging condition, Inverse charge current =1C5A;time: ≥ 90mins |
3 |
Short Circuit test |
No fire、 No explosion |
The battery to be fully charged with standard charging
condition, and short the positive and negative
terminals
|
4 |
Crush test |
No fire、No explosion |
A battery is crushed between two flat surfaces. The applied force is 13 kN±1kN by hydrocylinder, Once the maximum pressure has been obtained or voltage decrease to 1/3 of nominal voltage sharply, then release pressure. |
5 |
Shock test |
No fire、No explosion |
The full charged battery is fixed on shock table, to force a certain shock to three mutual vertical direction, in initial 3ms, the min. average acceleration is 75gn,the peak acceleration is between 125gn and 175gn. |
6 |
Heating test
|
No fire、No explosion |
The cells are fully charged with standard charging condition, and put into incubator with nature air or cycled air convected, heat battery by velocity of 5°C ±2°C/min to 130°C±2°C,and maintain for 10mins. |
7 |
Temperature
|
no leakage, no fire, no explosion |
The fully charged batteries are placed in a test chamber and subjected to the following cycles: a) Raising the temperature to 75°C ±2°C within 30 minutes and maintaining this temperature for 6 hours. b) Reducing the temperature to minus 40°C ±2°C within 30 minutes and maintaining this temperature for 6 hours. c) Repeating the sequence for a further 9 cycles. d) After the 10th cycle, storing the batteries for 24 hours prior to examination. |