MOQ | 30 Piece/Pieces |
Application | Liners Of Industrial Furnace | Thickness | 13~100mm |
Width | 600/1000mm | Length | 900/1000/1200mm |
Grade | HA (High Aluminum) | Chemical Composition | Al2O3,SiO2 |
Ultimate Strength (u2265 MPa) | 0.5 | Working Temperature | 1360 |
Fiber Diameter | 3~4.5um | Thermal Conductivity | 0.13-0.19 (w/m.k)(800-1000C) |
Shrinkage (1800u2109, 3h) | -3 (24hours) | Place of Origin | Jiangsu, China |
Model Number | CT 1350 | Brand Name | Cera Tec |
Color | white | desity | 250-300 kg/m3 |
Al2O3 | 52-55% | Al2O3+SiO2 | 99 |
Package | Carton+Pallet | Rupture Strength(MPa) | 0.5 |
Linear Shrinkage after Firing%(u2103x24h) | Linear Shrinkage after Firing%(u2103x24h) | Thermal Conductivity(W/m.k) | Thermal Conductivity(W/m.k) |
Ignition Lost(at 1000u2103x5hr)Lol% | 8 | MOQ | 20 pcs |