MOQ | 1 Ton/Tons |
Place of Origin | Henan, China | Shape | Powder |
Material | Alumina Block | SiO2 Content (%) | * |
Al2O3 Content (%) | 57%-70% | MgO Content (%) | Traces |
CaO Content (%) | Traces | Refractoriness (Degree) | Common (1580u00b0< Refractoriness< 1770u00b0) |
CrO Content (%) | Traces | SiC Content (%) | Traces |
Model Number | steel making | Brand Name | Lite |
Raw material | Mullite | Binder | CA70 refractory cement |
Bulk density | 2.35-2.8g/cm3 | Bending Strength 110u00b0C | 6.5-8.1Mpa |
Bending Strength 1000u00b0C | 7.2-10.1Mpa | Compressive strength 110u00b0C | 32-48Mpa |
Compressive strength 1000u00b0C | 42-80Mpa | Water content to mixture | 5%-7.8% |
Using parts | Furnace lining ,roof,wall etc | Feature | High strength and lower linear change |
No.171,Zhongyuan Road,Zhongyuan District,Zhengzhou,Henan,China