Place of Origin | Anhui, China | Brand Name | Bravo-Han |
Model Number | Modified PA | Material | Polyamide 6/66 Nylon6/66 Pa6/66 |
Color | Customize | Type | Granule |
Sample | Avaiable | Product name | Modified PA |
Usage | Injection Molding Products Automobile Part | Form | Plastic Pellets |
Package | Waterproof | Quality | Top Quallity |
Advantage | Nylon Product |
PA6 G30 BK03 30% GF
|
||||||||
Properties
|
Test Standard
|
Test Condition
|
Units
|
Typical Values
|
||||
Specific Gravity
|
GB/T1033
|
23 ℃
|
/
|
1.35
|
||||
Melt Flow Rate
|
GB/T 3682
|
230℃, 2.16KG
|
g/10min
|
25
|
||||
Mold Shrinkage
|
GB/T 15585
|
23 ℃
|
%
|
0.3~0.7(0.5)
|
||||
Mechanical Properties
|
||||||||
Tensile Strength
|
GB/T 1040
|
50 mm/min, 23 ℃
|
Mpa
|
135
|
||||
Flexural Strength
|
GB/T 9341
|
2 mm/min, 23 ℃
|
Mpa
|
200
|
||||
Flexural Modulus
|
GB/T 9341
|
2 mm/min, 23 ℃
|
Mpa
|
6500
|
||||
IZOD Impact
|
GB/T 1843
|
23 ℃
|
KJ/㎡
|
15
|
||||
Notched
|
GB/T 1843
|
23 ℃
|
KJ/㎡
|
NB
|
||||
Thermal Preperties
|
||||||||
H.D.T
|
GB/T 1634
|
0.45MPa, 3.2mm
|
℃
|
220
|
||||
Flammability
|
/
|
HB
|