High hardness strength
High wear resistance
Good tensile strength and fatigue resistance
Good thermal and chemical stability
Place of Origin | Anhui, China | Brand Name | Bravo-Han |
Model Number | Modified POM | Material | Polyoxymethylene (POM) |
Grade | Injection | Shape | Pellet Resin Granule |
Feature | High Temperature Resistance | Product name | POM Plastic Granules |
Application | Automobile Accessory | Form | Grain |
Sample | Provided | Color | White Black |
Quality | Top High |
Property
|
Test Method
|
Typical Value
|
Unit
|
Melt Flow Rate
|
ISO 1133 @ 190℃/2.16kg
|
1.6
|
g/10 min
|
Melt Flow Rate
|
ISO 1133 @ 210℃/2.16kg
|
3.7
|
g/10 min
|
Density
|
ISO 1183
|
1.19
|
g/cm3
|
Water vapor transmission rate
|
ASTM E96 @ 40℃ 90RH
|
1.3
|
|
Oxygen transmission rate
|
@ 20℃ ORH
|
0.0059
|
|
Oxygen transmission rate
|
@ 20℃ 65RH
|
0.0079
|
|
Oxygen transmission rate
|
@ 20℃ 85RH
|
0.03
|
|
Tensile Strength at Break
|
ISO 527@ 23℃
|
34
|
Mpa
|
Tensile modulus
|
ISO 527@ 23℃
|
2700
|
Mpa
|
Elongation at Break
|
ISO 527@ 23℃
|
15
|
%
|
Flexural modulus
|
ISO 178@ 23℃
|
4800
|
Mpa
|
Simply Supported Beam Unnotched Impact
|
ISO 179
|
2
|
Kj/㎡
|
Hardness
|
ISO 2023
|
90
|
|
Crystalliztion temoerature
|
ISO 11357
|
158
|
|
Glass transition temperature
|
ISO 11357
|
57
|
℃
|
Melting temperature
|
ISO 11357
|
1183
|
℃
|