Bimetallic Screw Barrel Tin Screw Tips Injection Molding Screw Tips

Quick Details (View All)

Model NO.	bimetallic screw barrel	Linearity of Screw	0.015mm
Surface Roughness	Ra0.4	Screw Barrel	Bimetallic Screw Barrel for Injection
Nitrided Hardness	950-1050hv	Nitrided Layer Depth	0.5-0.8mm
Transport Package	Film Wrapped in Wooden Case	Specification	ISO9001: 2008
Trademark	Zhongyang	Origin	China(Mainland) Zhejiang
HS Code	84779000	Production Capacity	200 Sets/Month

Product Details

Product Description

Bimetallic Screw Barrel for Injection Molding Machine, injection screw barrel, bimetallic screw barrel, Injection screw tips

Specification:
Screw diameter: Φ 20mm-Φ 220mm
Maximal length: 8000mm
Barrel diameter: Φ 20mm-Φ 220mm
Maximal length: 4000mm

Different bimetallic alloys are available for different raw materials.

Base Materials:
(1)38CrMoAlA(JIS SACM645)
(2)42CrMo(AISI 4140)
(3)9Cr18MOV

Mould clamping force: 250T-3200T
Shot weight: 30G-30000G

Bimetallic alloy materials:
1)Fe-based alloy
2)Ni-based alloy/Deloro alloy
3)Co-based alloy
4)NiCo-based alloy
5)Tungsten carbide/Wolfram carbide

Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting

Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000HV
Nitrided brittleness: Less than grade 1
Surface roughness: Ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: >=950HV
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm

Warranty and service: 1 year

Experienced manufacture, we will be the best choice.

Technical Parameter For Extruder Machine
Base Material	1)38CrMoAlA(JIS SACM645);2)Cr12MOV(JIS SKD-11) ; 3)4Cr5MoSiV1(JIS SKD-61) ;4)42CrMo(AISI 4140)
Bimetallic Alloy Materials	1)Fe-based alloy 2)Ni-based alloy/Deloro alloy 3)Co-based alloy 4)NiCo-based alloy 5)Tungsten carbide/Wolfram carbide
Double-alloy level	Level A - containing Tungsten of 40% Level B - containing tungsten of 25% Level C - containing tungsten of 9.5%
Surface Treatment	Heat Treatment High Frequency Treatment Nitriding treatment(120 Hours): Depth of Nitrided Layer: 0.5-0.8 mm Hardness of Nitrided Layer: 900-1020Hv (HRC56°-65°) Hard Chrome Plating treatment: Thickness of Hard Chrome Plating Layer: 0.05-0.10mm Hardness of Hard Chrome Plating Layer: ≥ 950HV Nickel alloy plating.treatment: Bimetallic Barrel/Cylinder: Centrifugal Casting (Inlay Alloy) Bimetallic Screw: Plasma Alloy Coating Spraying Depth of Bimetallic Layer: >2mm Hardness of Bimetallic Layer: HRC55°-72° Spraying corrosion wear-resisting dual metal layers
Basic information	Roughness of the surface:Ra0.4um Linearity of the screw: ≤ 0.015mm Linear axis limit: ≤ 0.02mm Hardness after Hardening & Tempering: HB240-280 Fragility of Nitration: ≤ Two class
Material Application	1)General Plastics 2)ABS,PA,PC,PE,PET,PP,PS,EVA,PU,PVC,U-PVC,etc 3)PA + GF(Glass Fiber) 4)Flame-resistant Reinforced Plastics 5)Modified Engineering Plastics 6)All kinds of Mixed Recycled Material(in Scrap or Granule), PVC + 30% CaCo3, etc