Aluminum Silicate Wool Felt / Board (Ceramic Fiber Felt / Board)
Standard | High Purity | High Aluminum | Zirconium | |
Apply Temperature(℃) | 1000 | 1100 | 1200 | 1350 |
Color | Pure White | Pure White | Pure White | Pure White |
Density(kg/m3) | 96-128 | 96-128 | 96-128 | 96-128 |
Linear shrinkage rate %(Constant temperature for 24 hours,density 128kg/m3) |
-3 1000℃ |
-3 1100℃ |
-3 1200℃ |
-3 1350℃ |
Thermal Conductivit (W/m*k) Bulk density(128kg/m3) |
0.09-400℃0.16-800℃0.20-1000℃ | 0.09-400℃0.16-800℃0.20-1000℃ | 0.12-600℃0.20-1000℃ | 0.12-600℃0.20-1000℃ |
Fiber Length | 100--150mm | 100--150mm | 100--150mm | 100--150mm |
Aluminosilicate refractory module assembly
Normal | Standard | High Purity | High Aluminum | Zirconium | ||
Apply temperature ℃ | 1000 | 1100 | 1150 | 1260 | 1350 | |
Color | White | White | Pure white | Pure white | Pure white | |
Thermal Conductivity (W/m*k) |
200℃ 400℃ 600℃ |
0.045 0.080 0.165 |
0.055 0.105 0.165 |
0.054 0.105 0.165 |
0.054 0.103 0.165 |
0.053 0.100 0.160 |
Slag Content % | 15.2max | 15.2max | 15.2max | 13max | 13max | |
Fiber diameter | 2-4 | 2-3 | 2-3 | 2-3 | 2-3 |
Aluminum Silicate Shell
Aluminum silicate fiber flat felt | ||
Apply Temperature(℃) | 1000max | |
Bulk density(kg/m3) | 140 | |
Thermal conductivity(w/m*k) | 20℃ | 0.034 |
400℃ | 0.09 | |
600℃ | 0.12 | |
Slag content(%)(diameter 0.21mm min) | 15.4 | |
Tensile strength(kg/m2) | 2.66 | |
Permanent linear shrinkage rate (Constant temperature for 24 hours) | -3.5(600℃) |