Place of Origin | Jiangsu, China | Brand Name | Lutong |
Model Number | SG0104 | Application | industry |
Surface Treatment | Mill Finish | Shape | rectangular |
Technique | EXTRUDED | Dimensions | 42 |
Grade | 6000 series | Hardness | 12HW |
Alloy Or Not | Is Alloy | Al (Min) | 98.8% |
Yield (≥ MPa) | 180 | Temper | T3 - T8 |
Ultimate Strength (≥ MPa) | 205 | Wall thickness | 6mm |
Weight | 0.68kg/m |
1.Details
Material |
6063,6060,6061,6005 |
Temper |
T5,T6 |
Surface treatment |
Anodized, Mill Finish,Powder Coated,Sandblasted |
Length |
as required |
Standard Dimension |
6mm,10mm,14mm,18mm,40mm,50mm,57.15mm,100mm,200mm,230mm,etc |
Package |
1)inner plastic paper interleaving each bar to protect the surface 2)20 pieces bar one small package 3)outer fixed and protected by plywood, carton or wooden pallets |
Payment terms |
TT or LC at sight |
Mould fee |
standard design no fee, new design mould fee to be prepaid before production, normally the fee to be returned when order quantity reach 5 tons. |
Delivery time |
10-12 days after order confirmation, first 7 days for open new mould |
Certification |
ISO 9001:2008;ISO14001:2004;SGS |
Capacity |
3000 tons per month |
2.Primary Technical Data
1)Chemical composition
Alloy |
Si |
Fe |
Cu |
Mn |
Mg |
Cr |
Zn |
Ti |
Impurity |
Al |
6061 |
0.4-0.8 |
0.70 |
0.15-0.4 |
0.15 |
0.8-1.2 |
0.04-0.35 |
0.25 |
0.15 |
0.15 |
Rest |
6063 |
0.2-0.6 |
0.35 |
0.1 |
0.1 |
0.45-0.9 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
6060 |
0.3-0.6 |
0.1-0.3 |
0.1 |
0.1 |
0.35-0.6 |
- |
0.15 |
0.1 |
0.15 |
Rest |
6005 |
0.6-0.9 |
0.35 |
0.1 |
0.1 |
0.4-0.6 |
0.1 |
0.1 |
0.1 |
0.15 |
Rest |
2)Mechanical property
Alloy |
Temper |
Tensile strength |
Yield strength |
Elongation |
6061 |
T6 |
≥ 265Mpa |
≥ 245Mpa |
≥ 8% |
6063 |
T5 |
≥ 160Mpa |
≥ 110Mpa |
≥ 8% |
T6 |
≥ 205Mpa |
≥ 180Mpa |
≥ 8% |
3)Anodized
Grade |
Anodizing thickness |
Hole scaling quality of oxide layer |
|
Average thickness |
Local thickness |
P. Cr acid-erosion weight less method |
|
AA10 |
≥10um |
≥8um |
≤30 mg/d m2 |
AA15 |
≥15um |
≥12um |
4)Powder coated
Coating thickness |
Coating impress rigidity |
Adhesive force of coating layer |
40-120um |
Indentation hardness>80 |
0 grade |