MOQ | 3 Ton/Tons |
Grade | 400 Series | Standard | JIS, AISI, ASTM, GB, DIN, EN |
Width | 10-1500mm | Length | coils |
Place of Origin | Jiangsu, China | Brand Name | Fushun |
Model Number | SUS440C 440C S44004 1.4125 X105CrMo17 | Technique | Cold Rolled |
Application | cutting | Certification | ISO |
Tolerance | ±1% | Processing Service | Bending, Decoiling, Punching, Cutting |
Dimensions | 20-150 mm | Inspection | The third party is acceptable |
Trade term | FOB CFR CIF | Payment | TT, LC, OA |
Standard of 440C Stainless Steel and Equivalent
Steel Grades
|
||||||
Country
|
USA
|
BS & DIN
|
Japan
|
|||
Standard
|
ASTM A276
|
EN 10088
|
JIS G4303
|
|||
Grades
|
S44004/440C
|
X105CrMo17/1.4125
|
SUS440C
|
ASTM A276 440C Steel Chemical Composition and
Equivalent’s
|
||||||||||||||
Standard
|
Grade
|
C
|
Mn
|
P
|
S
|
Si
|
Cr
|
|||||||
ASTM A276
|
S44004/440C
|
0.95-1.20
|
≦1.00
|
≦0.04
|
≦0.03
|
≦1.00
|
16.0-18.0
|
|||||||
EN10088
|
X105CrMo17/1.4125
|
0.95-1.20
|
≦1.00
|
≦0.04
|
≦0.03
|
≦1.00
|
16.0-18.0
|
|||||||
JIS G4303
|
SUS 440C
|
0.95-1.20
|
≦1.00
|
≦0.04
|
≦0.03
|
≦1.00
|
16.0-18.0
|
ASTM 440C Stainless Steel Mechanical Properties
|
||||||||||
Tempering Temperature (°C)
|
Tensile Strength (MPa)
|
Yield Strength 0.2% Proof (MPa)
|
Elongation (% in 50mm)
|
Hardness Rockwell (HRC)
|
Impact Charpy V (J)
|
|||||
Annealed
|
758
|
448
|
14
|
269HB max
|
–
|
|||||
204
|
2030
|
1900
|
4
|
59
|
9
|
|||||
260
|
1960
|
1830
|
4
|
57
|
9
|
|||||
316
|
1860
|
1740
|
4
|
56
|
9
|
|||||
371
|
1790
|
1660
|
4
|
56
|
9
|
Physical Properties
|
||||||||||||||||||
Grade
|
Density (kg/m3)
|
Elastic Modulus (GPa)
|
Mean Coefficient of Thermal Expansion (mm/m/°C)
|
Thermal Conductivity(W/m.K)
|
Specific Heat
|
Electrical Resistivity (nW.m)
|
||||||||||||
0-100°C
|
0-200°C
|
0-600°C
|
at 100°C
|
at 500°C
|
0-100°C (J/kg.K)
|
|||||||||||||
440 C
|
7650
|
200
|
10.1
|
10.3
|
11.7
|
24.2
|
–
|
460
|