MOQ | 1 Ton/Tons |
Place of Origin | Hebei, China | Brand Name | FengYue |
Model Number | AlTi5C0.2 | Application | aluminium grain refinement |
Surface Treatment | Mill Finish | Grade | AlTiC |
Alloy Or Not | Is Alloy | Al Content (%) | 94.5% |
Powder Or Not | Non-powder | CERTIFICATION | ISO9001:2008 |
Shape | Rod ,wire coil , ingot,cut bar | Material | Al-5%Ti-0.2%C |
Application:
AlTiC aluminum titanium carbon. Additive when
melting ,simple to use and no corrosive effect, no
pollution during production and application
process, little application amount, high purity and
no inclusion like salt, great grain refining
effect, improvement surface quality, reduction
pinhole number and raising elongation. A necessary
new modification material used in producing the
aluminum alloy wheel hub of automobile and
motorcycle and aluminum plate ,sheet, foil and the
high performance aluminum casting of aeronautical
and astronautical,military enterprises.
1. No pollution in the production process of
aluminum titanium carbon
2. Without potassium fluoborate as raw material,
the Al-Ti-C master alloy is not easy to contain
salt inclusion.
3. During the casting process, the nucleation
particles are released, the equiaxed grains are
effectively refined, and the formation of columnar
grains is prevented
4. Without TiB2 agglomeration, reducing inclusion
content, eliminating surface oxide and defects
5. As for as the impact on the number of second
phase particles, under the same refining effect, it
can be introduced into smaller amount of hard
points by using Al-Ti-C master alloy to the melt,
so as to avoid the potential adverse effects, which
is more significative in the production of PS plate
or light gauge foil .
6. In the casting production of boron-free nuclear
industrial aluminum, Al-Ti-C grain refiner have
more advantage.
7. The addition amount of Al-Ti-C is generally less
than Al-Ti-B , so, we can save some cost by using
Al-Ti-C.
Chemical composition:
Ti:4.5-5.5% C;0.15-0.25% Fe:0.3%Max Si:0.2Max
Usage method :
Add temperature: 720-750℃
The addition amount: according to the actual
calculation of the experiment to determine their
own.
Method: put in the furnace or add online
Rod: 9.5-10mm in diameter, 500-1000mm in length, 1 tons / pallet or wooden case
Coil shape: diameter 9.5-10mm, 180-220 kg /coil, 3 coils/ pallet
Special shapes, specifications and packaging can be produced according to customers' requirements