MOQ | 1 Ton |
Place of Origin | Henan, China | Shape | Brick |
Material | Zirconia Corundum imported from Australia | SiO2 Content (%) | 13 |
Al2O3 Content (%) | 48 | MgO Content (%) | 0 |
CaO Content (%) | 0 | Refractoriness (Degree) | 1770u00b0< Refractoriness< 2000u00b0 |
CrO Content (%) | 0 | SiC Content (%) | 0 |
Model Number | TY-AZS33 36 41 | Brand Name | sunrise |
Processing Service | Cutting, Moulding | Name | Refractory Bricks for glass furnace frit furnace water glass furnace |
size | any size | Item | TY 41 |
ZrO2 | u226540.50% | Al2O3 | u226545.005 |
SiO2 | u226413.00% | Bulk density g/cm3 | u22654.00 |
Apparent Porosity % | u22641.2 | Cold Crushing Strength Mpa | u2265300 |
Exudation Temperature of Glass Phase | u22651410 |