Port | - |
Packaging | - |
Lead Time | - |
Grade | HAZ (High Aluminum Zirconium) | Application | Liners Of Industrial Furnace |
Thickness | 25/50 mm | Width | 610/600 mm |
Length | 7200/3600 mm | Chemical Composition | 72% Al2O3+28% SiO2 |
Ultimate Strength (u2265 MPa) | 0.04 | Working Temperature | 1500 |
Fiber Diameter | 3.1 | Shrinkage (1800 u2109, 3h) | 3 (hours) |
Thermal Conductivity | 0.23 | Density (kg/mu00b3 ) | 128 |
Model Number | 1600 | Brand Name | NATI |
Place of Origin | Shanghai, China (Mainland) | Color | white |