MOQ | 50 Units |
Port | Sichuan, China |
Packaging | Opp Bag, Custom Box Packaging |
Lead Time | 3 Weeks |
OEM | Available | Payment Terms | Bank Wire / PayPal / T/T |
Customization | Accept | Availibility | In Stock |
Place of Origin | China | Shape | Customized |
ITAM |
UNIT |
Si coated |
Antiblock silicon free |
Print level |
Test method |
THICKNESS OF FILM TESTED |
mm |
0.2~1.4 |
0.2~1.4 |
0.2~0.6 |
ASTM D |
DENSITY |
g/cm3 |
1.34 |
1.34 |
1.34 |
ASTM D792 |
HAZE |
% |
0.3(0.3mm) |
0.3(0.3mm) |
0.3(0.3mm) |
ASTM D1003 |
TOTAL LIGHT TRANSMITTANCE |
% |
91(0.3mm) |
91(0.3mm) |
91(0.3mm) |
ASTM D1003 |
TENSILE STRENGTH YIELD |
|||||
MD |
kg/cm2 |
>450 |
>450 |
>450 |
ASTM D638 |
TD |
kg/cm2 |
>450 |
>450 |
>450 |
|
TENSILE MODULUS OF AUTYOUNG |
|||||
MD |
kg/cm2 |
>17000 |
>17000 |
>17000 |
ASTM D638 |
TD |
kg/cm2 |
>17000 |
>17000 |
>17000 |
|
ELONGATION YILED |
|||||
MD |
% |
>3.0 |
>3.0 |
>3.0 |
ASTM D638 |
TD |
% |
>3.0 |
>3.0 |
>3.0 |
|
DART IMPACT |
g/mm |
>1600 |
>1600 |
>1600 |
ASTM D1709 |
LOAD CELL 15KN |
|||||
DIACLAMP |
|||||
THERMAL |
ISO 11357-1 |
||||
GLASS TRANSITION TEMPERATURE |
℃ |
78 |
78 |
78 |
|
CRYSTAL TEMPERATURE |
℃ |
138 |
138 |
138 |
|
MELITING TEMPERATURE |
℃ |
249 |
249 |
249 |
|
RECRYSTAL TEMPERATURE |
℃ |
190 |
190 |
190 |
|
Dyne |
≥40 |
ASTM D2578 |
No.150, Mingjiang West Road, Yibin City, Sichuan Province, China