Material | 100% Polypropylene | Use | CONCRETE, mortar |
Density | 0.91g/cm3 | Melting Point | 160 |
Fiber Length | 3,6,9,12,19MM | Elastic Modulus | 3500MPa |
Tensile Strength | 400-600 MPa | Ignition Points | 580 |
Elongation At Break | 30% | Acid, Alkali & Salt Resistance | Extremely Strong |
Place of Origin | Shanghai, China | Brand Name | KAIDU |
Model Number | PP FIBER | Length | 6,12MM |
Color | Raw White | Type | Monofilament Pp Fiber |
Polypropylene fiber is made of polypropylene particles by continuous hot extrusion processing. Due to destaticization and anti-ultraviolet treatment, it well-proportioned disperse in mortar and could function for a long time. According to different constucton part and different area, it mixed amount will be different, the mixed amount should be more when used in stronger impacting part and cold part.
material |
100% polypropylene |
elongation at break |
30% |
Fibre type |
Bunchy monofilaments |
specification |
3,6,9,12mm or customerize |
density |
0.91 |
tensile strength |
≥400mpa |
Acid and alkali |
High |
young modulus |
≥3.5Gpa |
Melting point |
About 160℃ |
fiber diameter |
31um |
conductivity for heat |
very low |
burning point |
580℃ |
Containing moist |