It is used for determining the cracking resistance of vulcanized or thermoplastic rubbers when subjected to dynamic or static tensile strain exposed at a man-made constant temperature to atmosphere containing given concentration of ozone in conformance with relevant specification.
Standards: JIS K 6259-1, ISO 1431-1, IEC 60811-2-1, GB/T 2951.21, GB/T 13642-1 etc
|
Test chamber inner dimension |
W500XH600XD500mm |
|
Test chamber Temperature & Humidity |
Temperature control range: 0℃~70℃ adjustable Temperature uniformity: +/- 2℃ Humidity control range: 20%RH~90%RH adjustable |
|
Ozone concentration |
10~1000pphm +/- 10% pphm adjustable |
|
Ozone gas flow velocity |
12~16mm/s |
|
Velocity of ozonized air |
600mm/s+/- 100mm/s |
|
Test time |
0~999H/M/S |
|
Dynamic testing device |
Turnable sample rack stretch frequency: 0.5Hz Sample stretched cyclic between 0 to 10% or other specify stretch ratio Continuous or intermittent dynamic stretching available Sample rack rotating rotates at the specified speed available |
|
Static test device |
After the sample is stretched by 20% or other specified ratio, it is fixed on the sample holder, and the sample holder is rotated at a specific rate to fully expose it to the specified ozone gas. After reaching the predetermined time Observe whether the surface of the sample is cracked |
|
Sample rack rotating velocity |
20mm~25mm/s or adjustable at will |