Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAH

MOQ	500 kg
Port	shanghai
Packaging	25kg/bag
Lead Time	7days

Contact Now

Product Details

Hydroxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers

Hydroxyl Modified Vinyl Chloride, Hydroxyl Modified Vinyl Acetate Terpolymers

New grade MVAH: It is white powder,ester soluble with colorless and transparent solution,and it has with excellent solvent release,film-forming,dispersibility,color contrast property and wettability,moreover, it has excellent dispersibility in pigment and has very good adhesive force on PET,which can completely replace Solbin A grade of Nissin and T5HX grade of Kaneka etc.

MVAH Vinyl Resin Quality standard (XHQB-10).

No.	Item	Index	Test method
1	Appearance	White powder	By visual
2	Whiteness	≥80	GB2913-82
3	Composition % by Wt	Vinyl Chloride 90±1%	GB/T7139-2002
		Vinyl Acetate 3±1%	ISO1159-1978
		Vinyl Alcohol 7±0.5%
4	Reactive Functionality (Hydroxyl %)	1.8-2.3%
5	Hydroxyl Value	70-76	ISO2554-1974
6	K Value	46-48.	GB/T 3401-2007
7	Viscosity No. ml/g	52-56	GB/T 3401-2007
8	Glass transition Temp ℃	About 79	GB11998-89
9	Average Molecular Wt	About 27000.	Calculated by the Viscosity No.
10	% by wt, through 60 mesh	100%	GB/T6003.1
11	Apparent density (g/ml)	≥0.5	GB20022-2005
12	Volatilization (%)	≤1%	GB/T2914-1999
13	Impurity Particle No. /100g	≤20	GB9348-88
14	20% resin in EA or MEK	Colorless and Transparent or Yellowish	By visual

Application:

MVAH new grade is mainly used for application gravure plastics composite printing inks,PU inks,can sealed coatings,plastic coatings,magnetic tape and carbon tape adhesive,car refinishing paint etc.

Package, storage and transportation:

* In kraft bag, lined with pp bags of 25kgs net, with PE inner bag.

* Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and caution against wet.

* Must be transported in clean vehicle with awning and keep away from moisture.

* It is NOT hazardous article, and the shelf life is one year from the production date.