Cordierite Diesel Particulate Filter(DPF)
The most common filter is made of cordierite. Cordierite filters provide excellent filtration efficiency, are relatively inexpensive (comparison with Sic wall flow filter). The major drawback is that cordierite has a relatively low melting point.
Original: Jiangsu, China
Certification:TS16949 ISO9001
Price: Negotiable
Material: cordierite
Payment term: TT, LC
Delivery date: Negotiable
Packing: export standard
Warranty: 3 months
MOQ:Standard size 1 piece /Custom size from 100 pieces
Shape:custmoized
Property (uncatalyzed) |
100/17 |
200/12 |
|||
Cell density |
cpsi |
100 |
200 |
||
cpscm |
15.5 |
31 |
|||
Wall thickness |
inch |
0.017 |
0.012 |
||
mm |
0.432 |
0.305 |
|||
Open frontal area (OFA), % |
34.5 |
34.5 |
|||
Geometric surface area (GSA) |
Inch2 |
33.3 |
47 |
||
m2/l |
1.31 |
1.85 |
|||
Hydraulic diameter |
Inch |
0.083 |
0.059 |
||
mm |
2.11 |
1.49 |
|||
Modulus of rupture (psi/cpscm) |
350 |
300 |
|||
Porosity (%) |
48 |
48 |
|||
Coefficient of thermal expansion |
5 |
5 |
|||
102cm (20-800) --maximum average |
|||||
Mean pore size (micron) |
13 |
13 |
|||
Melting temperature |
1460 |
1460 |
|||
Parameters |
Unit |
Data |
|||
Material: Cordierite |
wt% |
≥90 |
94 |
||
Coefficient of Thermal Expansion(20-800°C) |
cm/cm/ °C |
≤1.8×10-6 |
≤1.5×10-6 |
||
Thermal Stability(20-650°C) |
times |
≥1 |
3 |
||
Soften Temperature |
°C |
≥1420 |
1440 |
||
Compression Strength |
Lengthways |
MPa |
16 |
16.9 |
|
Horizontal |
MPa |
5 |
6.2 |
||
Specific Weight |
Kg/L |
0.45-0.55 |
0.45-0.5 |
||
Porosity |
% |
40-45 |
41 |
||
Water-absorbing rate |
% |
23-25 |
23.8 |