Polyolefin Elastomer 8200
Product Description
ENGAGE™ 8200 Polyolefin Elastomer is an ethylene-octene copolymer that has excellent flow characteristics and performs well in a wide range of general-purpose thermoplastic elastomer applications.
ENGAGE 8200 provides superb impact properties in blends with polypropylene (PP) and polyethylene (PE), especially in applications requiring slightly higher melt flow. ENGAGE 8200 also provides high filler loading capability, excellent electrical properties, and (when cross-linked) exceptional heat aging, compression set, and weather resistance properties.
Main Characteristics:
• Pellet form
• Excellent flow characteristics
• High filler loading
• Excellent electrical properties
• Improved impact in polypropylene and polyethylene
• Exceptional heat aging, compression set, and weather resistance when cured
Applications:
Physical Nominal Value Unit Test Method
Density / Specific Gravity 0.870 g/cm³ ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) |
5.0 g/10 min |
ASTM D1238 |
Mooney Viscosity (ML 1+4, 121°C) |
8 MU |
ASTM D1646 |
Mechanical |
Nominal Value Unit |
Test Method |
Tensile Modulus - 100% Secant 2 (Compression Molded) |
2.30 MPa |
ASTM D638 |
Tensile Strength 2 (Break, Compression Molded) |
5.70 MPa |
ASTM D638 |
Tensile Elongation 2 Break, Compression Molded |
1100 % |
ASTM D638 |
Flexural Modulus 1% Secant : Compression Molded |
10.9 MPa |
ASTM D790 |
2% Secant : Compression Molded |
10.8 MPa |
|
Elastomers |
Nominal Value Unit |
Test Method |
Tear Strength 3 |
37.1 kN/m |
ASTM D624 |
Hardness |
Nominal Value Unit |
Test Method |
Durometer Hardness Shore A, 1 sec, Compression Molded |
66 |
ASTM D2240 |
Shore D, 1 sec, Compression Molded |
17 |
Thermal |
Nominal Value Unit |
Test Method |
Glass Transition Temperature |
-52.0 °C |
Internal Method |
Vicat Softening Temperature |
45.0 °C |
ASTM D1525 |
Melting Temperature (DSC) 4 |
60.0 °C |
Internal Method |
Peak Crystallization Temperature (DSC) |
45.0 °C |
Internal Method |
Notes
1 Typical properties: these are not to be construed as specifications.
2 510 mm/min
3 Die C
4 10°C/min