Aramid Fiber

Product Details

Introduction

Bannor, founded in 2017, is committed to manufacturing high-quality aramid fibers. With our own independent intellectual property rights, we specialize in high-strength and high-modulus para-aramid fibers ranging from 200 to 9000 Denier, which are widely used in hoses, optical cables, tire cords, and bulletproof materials. By 2022, Bannor is capable of producing over 5000 tons of para-aramid annually, with plans to expand the capacity to 9000 tons per year in the future. To better serve our customers, we also process our own filaments into staple fiber, short-cut fiber, and pulp, ensuring quality and exploring new application fields with our powerful R&D team. With a firm belief in this industry and technology, Bannor aims to be the largest para-aramid manufacturer in China and your most reliable supplier globally.

Aramid Fiber Series Products

Bannor Aramid Staple

Bannor Aramid Staple staple fibers are made from filaments, which are washed, crimped and cut and then treated by surface treatment. Staple fibers are widely used in high-end yarn, blended yarn, needle-spun felt and non-woven industry.

Specification	DPF	Length	Crimp Percentage	Finish	Moisture Regain
Specification	[denier][dtex]	[mm]	[ea/inch]	[%]	[%]
BN 213	1.5/1.67	38.0	7	0.35	7.0
BN 215	1.5/1.67	51.0	7	0.35	7.0
BN 217	1.5/1.67	76.0	7	0.35	7.0
BN 223	2.3/2.50	38.0	6	0.35	7.0
BN 225	2.3/2.50	51.0	6	0.35	7.0
BN 227	2.3/2.50	76.0	6	0.35	7.0
BNB 213	1.5/1.67	38.0	7	0.35	7.0
BNB 215	1.5/1.67	51.0	7	0.35	7.0

Bannor Aramid Short-Cut

Bannor Aramid Short-cut fibers are produced by cutting filaments, which are suitable for aramid paper, plastic reinforcement and various composite materials.

Specification	DPF	Length	Break Strength	Finish	Moisture Regain
Specification	[denier][dtex]	[mm]	[ea/inch]	[%]	[%]
BN 211C	1.5/1.67	1	21	0	7.0
BN 213C	1.5/1.67	3	21	0	7.0
BN 216C	1.5/1.67	6	21	0	7.0
BN 221C	2.25/2.50	1	21	0	7.0
BN 223C	2.25/2.50	3	21	0	7.0
BN 226C	2.25/2.50	6	21	0	7.0

Bannor Para-Aramid Pulp

Bannor Para-aramid pulp is made from filament yarn whose composition is poly(para-phenylene terephthalamide). After a series process of cutting, grinding and suspending in water, the fiber is fibrillated into pulp. The pulp not only inherits the high- strength, high-modulus, high-temperature resistance, abrasion resistance and excellent chemical stability from para-aramid fiber, but also has high dispersibility, specific surface area and grip force to provide reinforcement and viscosity control under shear stress.

Specification	C.S.F.	Specific Surface Area	Average Strength	Thermal Decomposition Temperature	Moisture Content
Specification	[ml]	[m²/g]	[mm]	[℃]	[%]
BN 230	320-420	7-10	0.6-0.8	550	7.0
BN 240	420-500	9-15	0.6-1.0	550	7.0
BN 250	500-800	9-14	0.8-1.2	550	7.0
BN 260	600-880	8-13	1.0-1.4	550	7.0

Bannor Aramid Powder

Bannor aramid powder is a high-grade, multifunctional material, primarily composed of poly(p-phenylene terephthalamide) (PPD-T). This powder is produced through a series of sophisticated processes, including high-temperature treatment, fine milling, and special dispersion techniques. Compared to traditional aramid pulp, the aramid powder features finer particle size and higher surface activity, demonstrating superior performance in various applications.

Specification	Particle Size	Thermal Decomposition Temperature	Moisture Regain
Specification	[mm]	[℃]	[%]
BN 110	D97≤1.40	550	2.0
BN 120	D99≤0.125	550	2.0