Material | 100% Polypropylene | Use | Filling Material, Spinning, Non-Woven Fabric, CONCRETE |
Density | 0.90-0.92 g/cm3 | Melting Point | 160 - 170 |
Fiber Length | 50MM | Elastic Modulus | 3.5Gpa |
Tensile Strength | 600-700 MPa | Ignition Points | 590u2103 |
Elongation At Break | 400-600MPa | Acid, Alkali & Salt Resistance | Strong |
Place of Origin | GUA | Color | White |
MOQ | 1TON | Key words | PP s Fiber |
Application | Concrete Reinforcement | Length | 3-12mm |
Feature | Anti-cracking Agent | Packing | PP Woven Bags |