Factory Direct Sales Pre-Baked Carbon Anode For Alunimun

FOB Price 508 - 605 USD / t

Quantity	20 - 100
Price	508

MOQ	20 t
Port	Tianjin port
Packaging	wooden box
Lead Time	15 working days

Quick Details (View All)

Brand name	BENHONG	Place of Origin	High end products Leverage
Thermal Exposure	<4*10	current density	> 0.8A/cm2
Electrical Resistivity	55-56μΩm	Size and Shape	As your request

Product Details

pre-baked consumable Carbon Anode made from petroleum coke, and coal tar pitch,through mixing,forming and baking processes,be used as anodes in cells of Primary Aluminum Smelter. Pre-baked Carbon Anodes Produced

by Carbon has the property of lower Ash content Lower Sulfur content,and Higher Compress strength.

CO2 Reactivity Residue can reach above 91%, and Air Reactivity can reach above 96%; the life-span in cells of aluminum electrolysis is 30-33days, with Jining’s anodes the carbon consumption required for producing one-ton primary aluminum will reduce by about 30Kg than using Pre-baked Carbon Anodes produced by other suppliers. Higher thermal shock Resistance;Thermal Exposure: <4*10;Heat Conductive <3W/ml;higher current density; current density:> 0.8A/cm2;lower Electrical Resistivity Electrical Resistivity: 55-56μΩm

ANODE SPECIFICATION

Series	PROPERTY	Unit	Standard method	Range
1	Real Density	g/cm3	ISO 8004	2 Min
2	Apparent Density	g/cm3	ISO 12985	1.52-1.58
3	Air permeability	npm	ISO 15906	0.5-1.5
5	Compressive Strength	N/mm2	ISO 18515	40-48
6	Youngs moudle	Gpa	ISO 12989	4-5.5
7	Flexural Strength	N/mm2	ISO 12986	8 - 10
8	Spe. Elec. Resistance	µΩm	ISO 11713	55-62
9	Cof. Lin . Thermal	µm/(k.m)	ISO 14420	3.75-4.5
10	Thermal Conductivity	W/(k.m)	ISO 129087	3-4.5
11	ASh	%	ISO 8005	0.5 Max
12	Air Reactivity residue dust Lost	% % %	ISO 12989-1	75 – 85 4 - 8 10 - 20
13	Co2 Reactivity residue dust lost	% % %	ISO 12988-1	84 – 95 3 - 8 6 - 14
14	Elements S V Fe F Ca Al Ni SI	% ppm // // // // //	ASTM D6376	0.5 – 2.5 30 - 320 100 – 600 150 – 600 50 – 200 150 – 600 40 – 200 50 - 300