Co-based amorphous ribbons with thickness of 15 to 25 μm (specified by the customer) and a width of 20, 25, 30 mm in the original version after spinning. It can be cut to a width from 0.7 up to 30 mm as per customer request.
Alloy properties ASaturation induction B10, T | 1,0 | 0,9 | 0,85 | 0,75 | 0,68 | 0,66 | 0,60 | 0,55 |
Coercitive force Hc, A/m | 4,0 | 2,0 | 1,6 | 1,2 | 0,24 | 0,24 | 0,24 | 0,16 |
Relative permeability µ @ 10 kHz | 1400 | 2200 | 3300 | 10000 | 35000 | 50000 | 70000 | 120000 |
Max. permeability, µ max, ×103 | - | - | - | 500 | - | 800 | 1000 | 1200 |
Ore specific loss, W/kg @ 0.2T: 10 kHz 100 kHz |
1,5÷2,0
50÷60 |
1,5÷2,0
45÷55 |
1,5÷2,0
35÷45 |
1,5÷2,0
30÷40 |
1,0÷1,5
20÷30 |
1,0÷1,5
20÷30 |
1,0÷1,5
20÷25 |
0,5÷1,0
20÷25 |
Crystallization temperature Tcr, °C | 450 | 470 | 485 | 515 | 505 | 510 | 520 | 530 |
Curie temperature, Tc, °C | ≥ Ткр. | 430 | 380 | 350 | 275 | 265 | 235 | 200 |
Density γ, g/cm3 | 7,9 | 7,85 | 7,8 | 7,7 | 7,8 | 7,8 | 7,7 | 7,7 |
Squareness ratio, no more than* | 0,02 | 0,03 | 0,03 | 0,05 | 0,05 | 0,05 | 0,10 | 0,20 |
Squareness ratio, at least** | 0,95 | 0,95 | 0,95 | 0,9 | 0,9 | 0,9 | 0,9 | 0,9 |
Saturation magnetostriction λs, ×10-6 | 0,05 | 0,05 | 0,05 | 1,0 | 0,1 | 0,2 | -0,1 | 0,1 |